JCK-306 POLYAMIDE RESIN
CO-SOLVENT SOLUBLE
1.Summary
JCK-306 is polyamide resin soluble in co-solvent. Compared with other polyamide resin, JCK-306 have good gel resistance , superior dissolving power at room temperature after freezing, good flexible and very good adhesion because it select special formula. JCK-306 is applied to the preparation of various kinds of gravure ink used in printing on Polyethylene, Polypropylene, Terylene, Cellophane.
2. Quality index
Acid Value (mg KOH/g) ：≤5
Amine Value (mg KOH/g) ：≤4
Softening Point (℃) ：105±5
Viscosity (mpa·s/25℃) ：100-150
Co-solvent type： Viscosity measured in 40% NV with
Toluene and IPA (7：3) as solvent
3.Character
※excellent gelling resistance and superior dissolving power at room temperature after freezing
※greatly modify ink flowability and varnish wetting property
※good adhesion
※modify gloss, colour property of ink
4.Application Scope
Be applied to the preparation of various kinds of gravure ink used in printing on Polyethylene,Polypropylene, Terylene,Cellophane.
JCK-307 POLYAMIDE RESIN
CO-SOLVENT SOLUBLE
1.Summary
JCK-307 is polyamide resin soluble in co-solvent. Compared with other polyamide resin, JCK-307 have good gel resistance , superior dissolving power at room temperature after freezing, good flexible and very good adhesion because it select special formula. JCK-307 is applied to the preparation of various kinds of gravure ink used in printing on Polyethylene, Polypropylene, Terylene, Cellophane.
2.Quality index
Acid Value (mg KOH/g) ：≤5
Amine Value (mg KOH/g) ：≤4
Softening Point (℃) ：105±5
Viscosity (mpa·s/25℃) ：150-200
Co-solvent type： Viscosity measured in 40% NV with
Toluene and IPA (7：3) as solvent
3.Character
※excellent gelling resistance and superior dissolving power at room temperature after freezing
※greatly modify ink flowability and varnish wetting property
※good adhesion
※modify gloss, colour property of ink
4.Application Scope
Be applied to the preparation of various kinds of gravure ink used in printing on Polyethylene,Polypropylene, Terylene,Cellophane.
JCK-308 POLYAMIDE RESIN
CO-SOLVENT SOLUBLE
1.Summary
JCK-308 is polyamide resin soluble in co-solvent. Compared with other polyamide resin, JCK-308 have good gel resistance , superior dissolving power at room temperature after freezing, good flexible and very good adhesion because it select special formula. JCK-308 is applied to the preparation of various kinds of gravure ink used in printing on Polyethylene, Polypropylene, Terylene, Cellophane.
2.Quality index
Acid Value (mg KOH/g) ：≤5
Amine Value (mg KOH/g) ：≤4
Softening Point (℃) ：105±5
Viscosity (mpa·s/25℃) ：150-250
Co-solvent type： Viscosity measured in 40% NV with
Toluene and IPA (7：3) as solvent
3.Character
※excellent gelling resistance and superior dissolving power at room temperature after freezing
※greatly modify ink flowability and varnish wetting property
※good adhesion
※modify gloss, colour property of ink
4.Application Scope
Be applied to the preparation of various kinds of gravure ink used in printing on Polyethylene,Polypropylene, Terylene,Cellophane.
|
|
|
|
|